The Piezoresponse in WO3 Thin Films Due to N2-Filled Nanovoids Enrichment by Atom Probe Tomography

Abstract

Tungsten trioxide (WO3) is a versatile n-type semiconductor with outstanding chromogenic properties highly used to fabricate sensors and electrochromic devices. We present a comprehensive experimental study related to piezoresponse with piezoelectric coefficient d33 = 35 pmV����1 on WO3 thin films ~200 nm deposited using RF-sputtering onto alumina (Al2O3) substrate with post-deposit annealing treatment of 400 C in a 3% H2/N2-forming gas environment. X-ray diffraction (XRD) confirms a mixture of orthorhombic and tetragonal phases of WO3 with domains with different polarization orientations and hysteresis behavior as observed by piezoresponse force microscopy (PFM). Furthermore, using atom probe tomography (APT), the microstructure reveals the formation of N2-filled nanovoids that acts as strain centers producing a local deformation of the WO3 lattice into a non-centrosymmetric structure, which is related to piezoresponse observations.