Corrosion Fatigue Analysis in Power Steam Turbine Blade
(2023-03-08)The corrosion fatigue behavior of a martensitic stainless steel AISI 410 with 12% Cr, used in the fabrication of steam turbine blades at low pressure (L-P), was studied using the electrochemical noise technique (EN) under ... -
Crevices corrosion in cracks of aisi-410 used in steam turbines blades
(2018-06-12)In this paper the effect of temperature on corrosion crack propagation produced in a stainless steel AISI-410 type was studied. The previously cracked specimens through a rotatory machine were exposed in seawater during 5 ...